2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
168 (24400)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
185 (26800)
|
Bottles and Drums Use
|
Food
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
100 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
460 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
250 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Optical Performance, Processing
|
Melting Point, DSC (Dow Method) in °C(°F)
|
108 (226)
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4.87 J/cm3 (58.9 ft lb/in3)
|
Tensile Elongation at Break, MD
|
260 %
|
Tensile Elongation at Break, TD
|
540 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
21.6 (3130)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
16.4 (2380)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10.9 (1580)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10.8 (1560)
|