性能

app.properties.Title

Anti-block Yes
Slip true
Tie Layers No

typical.properties.Title

Density 0.904 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 560 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 730 g
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Haze (ASTM D1003) 3.2 %
Heat Seal Initiation Temp in °C(°F) 85 (185)
Melt Index ((g/10min @190°C/2.16 kg) (ASTM D1238)) 1
Melting Point, DSC (Dow Method) in °C(°F) 100 (212)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 21.9 (265 )
Tensile Elongation at Break, MD 590 %
Tensile Elongation at Break, TD 630 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 45.4 (6580)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 42.5 (6170)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 8.07 (1170)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 7.17 (1040)
Vicat Softening Point in °C(°F) 86 (187)