2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
139 (20200) (ISO 527-3)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
147 (21300) (ISO 527-3)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
480 g (ISO 7765-1/A)
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
560 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
910 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
0.85
|
Vicat Softening Point in °C(°F)
|
107 (225)
|