2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
207 (30000)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
234 (34000)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
66 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
280 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
3000 g
|
Fabrication Method
|
Blown Film Extrusion, Cast Film Extrusion
|
Functionality
|
Optical Performance, Processing
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
2
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
3.72 J/cm3 (45 ft /lb/in3)
|
Tensile Elongation at Break, MD
|
330 %
|
Tensile Elongation at Break, TD
|
550 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
21.6 (3130)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
17 (3460)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
13.5 (1960)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
13.5 (1960)
|