物性

app.properties.Title

Anti-block No
Cling Resins No
Performance Conventional
Slip No

product.use.formulating.properties.Title

Type Topsheet

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 2 mil - 138 (20000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 2 mil - 138 (19900)
Dart Drop Impact (ASTM D1709A) in grams (lbs) .8 mil - 130 g (ASTM D1709A), .8 mil - < 100 g (ASTM D1709B)2, 2 mil - 210 (ASTM D1709B), 2 mil - 330 (ASTM D1709A)
Density 0.918 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 2 mil - 790 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 2 mil - 1100 g
Enhanced LLDPE No
Fabrication Method Sheet Extrusion
Functionality Mechanical Performance
Gloss (45 degree) 95
Haze (ASTM D1003) 1 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2
Melting Point, DSC (Dow Method) in °C(°F) 123 (253)
Vicat Softening Point in °C(°F) 98.9 (210)