物性

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 500 (72500)
Density 0.939 g/cm3
ESCR-Environmental Stress Crack Resistance (10% IGEPAL) >2000 hr - 50˚C (122˚F)
Fabrication Method Pipe Extrusion
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) 22
Tensile Elongation at Break, MD 700 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 26.0 (3770)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 20.0 (2900)
Vicat Softening Point in °C(°F) 121 (250)