物性
key.properties.Title |
|
---|---|
Density | 0.923 g/cm3 |
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.75 |
app.properties.Title |
|
---|---|
Anti-block | No |
Collation Shrink Usage | Logistics, Retail |
Slip | No |
Tie Layers | No |
product.use.formulating.properties.Title |
|
---|---|
Type | Non-Breathable Blown Film |
typical.properties.Title |
|
---|---|
2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 175 (25600) |
2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 185 (26800) |
Dart Drop Impact (ASTM D1709A) in grams (lbs) | 170 g |
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 350 g |
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 260 g |
Fabrication Method | Blown Film Extrusion |
Functionality | Optical Performance, Processing |
Gloss (45 degree) | 58 |
Haze (ASTM D1003) | 9.2 % |
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) | 4 J/cm3 (48.3 ft lb/in3) |
Tensile Elongation at Break, MD | 390 % |
Tensile Elongation at Break, TD | 570 % |
Tensile Strength Break, MD (ASTM D882) in MPa (psi) | 25 (3630) |
Tensile Strength Break, TD (ASTM D882) in MPa (psi) | 23 (3340) |
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) | 11 (1600) |
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) | 11 (1600) |