物性
key.properties.Title |
|
|---|---|
| Density | 0.921 g/cm3 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 0.25 |
app.properties.Title |
|
|---|---|
| Anti-block | No |
| Collation Shrink Usage | Logistics, Retail |
| Slip | No |
| Tie Layers | No |
typical.properties.Title |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 128 (18600) |
| 2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 128 (18600) |
| Dart Drop Impact (ASTM D1709A) in grams (lbs) | 430 g |
| Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) | 270 g |
| Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) | 480 g |
| Fabrication Method | Blown Film Extrusion, Blown Film Extrusion |
| Functionality | Optical Performance, Processing |
| Tensile Elongation at Break, MD | 470 % |
| Tensile Elongation at Break, TD | 530 % |
| Vicat Softening Point in °C(°F) | 96 (205) |