2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1150 (167000)
|
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1150 (167000)
|
|
Brittleness Temperature in °C(°F)
|
< -76.1
|
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
3 hr
|
|
Fabrication Method
|
Injection Molding
|
|
Functionality
|
Mechanical Performance
|
|
Impact Strength in MPa (psi)
|
42 kJ/m2 (20 ft lb/in2) ASTM D1822
|
|
Tensile Elongation at Break, MD
|
250 %
|
|
Tensile Elongation at Break, TD
|
250 %
|
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
13.8 (2000)
|
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
13.8 (2000)
|
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
28.3 (4100)
|
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
28.3 (4100)
|