物性

app.properties.Title

Anti-block Yes
Slip Yes

typical.properties.Title

Dart Drop Impact (ASTM D1709A) in grams (lbs) 25 g
Density 0.925 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 200 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 100 g
Fabrication Method Cast Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 80
Haze (ASTM D1003) 4.4 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 6.4
Melting Point, DSC (Dow Method) in °C(°F) 113 (235)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) .910 J/cm3 (11 ft lb/in3)
Tensile Elongation at Break, MD 150 %
Tensile Elongation at Break, TD 440 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 32.4 (4700)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 12.8 (1850)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 13.9 (2010)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 11.4 (1660)
Vicat Softening Point in °C(°F) 96.1 (205)