2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
1170 (170000)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
1170 (170000)
|
Bottles and Drums Use
|
Food, Household Industrial Chemicals (HIC) / Agriculture Bottles, Personal Care, Pharma
|
Brittleness Temperature in °C(°F)
|
-60
|
ESCR-Environmental Stress Crack Resistance (10% IGEPAL)
|
220 hr
|
ESCR-Environmental Stress Crack Resistance (100% IGEPAL)
|
> 1100 hr
|
Fabrication Method
|
Blow Molding, Compression Molding
|
Functionality
|
Mechanical Performance
|
Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238))
|
27
|
Tensile Elongation at Break, MD
|
800 %
|
Tensile Elongation at Break, TD
|
800 %
|
Tensile Strength Break, MD (ASTM D638) in MPa (psi)
|
29 (4210)
|
Tensile Strength Break, TD (ASTM D638) in MPa (psi)
|
29 (4210)
|
Tensile Strength Yield, MD (ASTM D638) in MPa (psi)
|
24.8 (3600)
|
Tensile Strength Yield, TD (ASTM D638) in MPa (psi)
|
24.8 (3600)
|