Propiedades

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 800 (116000)
Density 0.939 g/cm3
ESCR-Environmental Stress Crack Resistance (10% IGEPAL) >3000 hr - 50˚C (122˚F)
Fabrication Method Blown Film Extrusion
Functionality Mechanical Performance
Impact Strength in MPa (psi) 82 J/m (1.5 ft-lb/in) - Notched Izod Impact (23˚C (73˚F))
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 0.38
Melt Index (g/10min @190°C/5.0 kg (ASTM D1238)) 0.38
Tensile Elongation at Break, MD >800 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 30.0 (4350)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 19.0 (2760)
Vicat Softening Point in °C(°F) 118 (244)