Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
180 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
290 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
230 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Optical Performance, Processing
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
4 J/cm3 (48.3 ft lb/in3)
|
Tensile Elongation at Break, MD
|
430 %
|
Tensile Elongation at Break, TD
|
660 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
18 (2610)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
16 (2320)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
10 (1450)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10 (1450)
|