2% Secant Modulus, MD (ASTM D882) in MPa (psi)
|
180 (26100)
|
2% Secant Modulus, TD (ASTM D882) in MPa (psi)
|
218 (31700)
|
Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
170 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
680 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
1100 g
|
Fabrication Method
|
Blown Film Extrusion
|
Functionality
|
Mechanical Performance
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
1.3
|
Melting Point, DSC (Dow Method) in °C(°F)
|
122 (252)
|
Vicat Softening Point in °C(°F)
|
108 (226)
|