Properties
key.properties.Title |
|
|---|---|
| Density | 0.95 g/cm3 |
| Melt Index ((g/10min @190°C/21.6 kg) (ASTM D1238)) | 33 |
| Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 33 |
app.properties.Title |
|
|---|---|
| Anti-block | No |
| Slip | No |
typical.properties.Title |
|
|---|---|
| 2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 1000 (145000) |
| 2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 1000 (145000) |
| Density Range | .940-.950 |
| Fabrication Method | Injection Molding |
| Functionality | Mechanical Performance |
| Structure Type | Monolayer, Multilayer |
| Tensile Strength Break, MD (ASTM D638) in MPa (psi) | 13.8 (2000) |
| Tensile Strength Break, TD (ASTM D638) in MPa (psi) | 13.8 (2000) |
| Tensile Strength Yield, MD (ASTM D638) in MPa (psi) | 26.9 (3900) |
| Tensile Strength Yield, TD (ASTM D638) in MPa (psi) | 26.9 (3900) |