Dart Drop Impact (ASTM D1709A) in grams (lbs)
|
27 g
|
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs)
|
310 g
|
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs)
|
80 g
|
Fabrication Method
|
Cast Film Extrusion, Extrusion Coating and Lamination
|
Functionality
|
Mechanical Performance
|
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238))
|
4.2
|
Melting Point, DSC (Dow Method) in °C(°F)
|
112 (234)
|
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3)
|
2.32 J/cm3 (28 ft lb/in3)
|
Tensile Elongation at Break, MD
|
220 %
|
Tensile Elongation at Break, TD
|
610 %
|
Tensile Strength Break, MD (ASTM D882) in MPa (psi)
|
31 (4500)
|
Tensile Strength Break, TD (ASTM D882) in MPa (psi)
|
17 (2470)
|
Tensile Strength Yield, MD (ASTM D882) in MPa (psi)
|
14.8 (2140)
|
Tensile Strength Yield, TD (ASTM D882) in MPa (psi)
|
10.9 (1580)
|
Vicat Softening Point in °C(°F)
|
95 (203)
|