Properties

app.properties.Title

Anti-block No
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 807 (117000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 807 (117000)
Brittleness Temperature in °C(°F) < -76.1
Density 0.95 g/cm3
Density Range .940-.950
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) 6 hr
Fabrication Method Injection Molding
Functionality Mechanical Performance
Impact Strength in MPa (psi) 273 kJ/m2 (130 ft lb/in2) ASTM D1822
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 12
Structure Type Monolayer, Multilayer
Tensile Elongation at Break, MD 600 %
Tensile Elongation at Break, TD 600 %
Tensile Strength Break, MD (ASTM D638) in MPa (psi) 13.8 (2000)
Tensile Strength Break, TD (ASTM D638) in MPa (psi) 13.8 (2000)
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) 23.4 (3400)
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) 23.4 (3400)