[{"values":[{"value":"日本語-Japanese","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文-Chinese Simplified","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English","languageCode":"en-us","link":"javascript:void(0);"}],"label":"JP","default":"ja-jp"},{"values":[{"value":"日本語-Japanese","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文-Chinese Simplified","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English","languageCode":"en-us","link":"javascript:void(0);"}],"label":"CN","default":"zh-cn"},{"values":[{"value":"日本語-Japanese","languageCode":"ja-jp","link":"javascript:void(0);"},{"value":"中文-Chinese Simplified","languageCode":"zh-cn","link":"javascript:void(0);"},{"value":"English","languageCode":"en-us","link":"javascript:void(0);"}],"label":"US","default":"en-us"}]

ATTANE™ 4404G Ultra Low Density Polyethylene Copolymer

An ultra-low density copolymer resin processable in blown and cast film, sheet extrusion, and coextrusion equipment designed for polyethylene.

Uses:

  • Industrial packaging
  • High performance machine wrap stretch films
  • General purpose machine wrap stretch film

Benefits:

  • Consistent cling performance
  • Excellent toughness
  • Outstanding optical properties
  • Good hot tack properties

Properties

These values are typical properties and are not intended for use in preparing specifications.

  • 2% Secant Modulus, MD (ASTM D882) in MPa (psi) Yes No 58.8 (8530) - 0.8 mil (20 µm)
  • 2% Secant Modulus, TD (ASTM D882) in MPa (psi) Yes No 63.0 (9140) - 2.0 mil (51 µm)
  • Anti-block Yes No false
  • Dart Drop Impact (ASTM D1709A) in grams (lbs) Yes No >850 g - 0.8 mil (20 µm)
  • Density (ASTM D792) Yes No 0.904 g/cm3
  • Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) Yes No 960 g - 2.0 mil (51 µm)
  • Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) Yes No 1100 g - 2.0 mil (51 µm)
  • Gloss (45 degree) Yes No 90 - 2.00 mil (50.8 µm) %
  • Haze (ASTM D1003) Yes No 1.80 - 2.00 mil (50.8 µm) %
  • Melt Index (g/10min @190°C/21.6 kg) Yes No 4.0 g/10minutes
  • Melting Point, DSC (Dow Method) in °C(°F) Yes No 124°C (255°F)
  • Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) Yes No 17.5 (211) - 2.0 mil (51 µm)
  • Slip Yes No false
  • Tensile Elongation at Break, MD Yes No 660 - 2.0 mil (51 µm) %
  • Tensile Elongation at Break, TD Yes No 710 - 2.0 mil (51 µm) %
  • Tensile Strength Break, MD (ASTM D882) in MPa (psi) Yes No 32.6 (4730) - 2.0 mil (51 µm)
  • Tensile Strength Break, TD (ASTM D882) in MPa (psi) Yes No 32.4 (4700) - 2.0 mil (51 µm)
  • Tensile Strength Yield, MD (ASTM D882) in MPa (psi) Yes No 6.76 (980) - 2.0 mil (51 µm)
  • Tensile Strength Yield, TD (ASTM D882) in MPa (psi) Yes No 6.34 (919) - 2.0 mil (51 µm)
  • Vicat Softening Point in °C(°F) Yes No 71.1°C (160°F)

ATTANE™ 4404G Ultra Low Density is a copolymer resin used in the skin layers of cast films. It offers excellent low temperature sealing properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4404G exhibits excellent stretchability, as well as good physical and cling properties. ATTANE™ 4404G can also be used in blown film coextrusion, where it is combined with other resins having excellent bubble stability, allowing ATTANE™ 4404G to be used as a sealant in multilayer film structures.

No Safety Data Sheets are available online for this material
Please Contact Dow for additional information.

No sales specification could be found for this material in selected language

ATTANE™ 4404G Ultra Low Density Polyethylene Copolymer
No Technical Data Sheets are available for this product
Please Contact Dow for additional information.

Choose

ATTANE™ 4404G Ultra Low Density Polyethylene Copolymer


No Regulatory Data Sheets are available for this product


ATTANE™ 4404G Ultra Low Density Polyethylene Copolymer
Please Contact Dow for distribution options available for this product.