Properties

app.properties.Title

Anti-block No
Cling Resins Yes
Performance Conventional, High Peformance
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 58.8 (8530) - 0.8 mil (20 µm)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 63.0 (9140) - 2.0 mil (51 µm)
Dart Drop Impact (ASTM D1709A) in grams (lbs) >850 g - 0.8 mil (20 µm)
Density 0.904 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 960 g - 2.0 mil (51 µm)
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 1100 g - 2.0 mil (51 µm)
Fabrication Method Sheet Extrusion
Functionality Mechanical Performance, Sealant (non-peelable)
Gloss (45 degree) 90 - 2.00 mil (50.8 µm)
Haze (ASTM D1003) 1.80 - 2.00 mil (50.8 µm) %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 4
Melting Point, DSC (Dow Method) in °C(°F) 124 (255)
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 17.5 (211) - 2.0 mil (51 µm)
Tensile Elongation at Break, MD 660 - 2.0 mil (51 µm) %
Tensile Elongation at Break, TD 710 - 2.0 mil (51 µm) %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 32.6 (4730) - 2.0 mil (51 µm)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 32.4 (4700) - 2.0 mil (51 µm)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 6.76 (980) - 2.0 mil (51 µm)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 6.34 (919) - 2.0 mil (51 µm)
Vicat Softening Point in °C(°F) 71.1 (160)