Properties

app.properties.Title

Anti-block No
Collation Shrink Usage Retail
Slip No

typical.properties.Title

2% Secant Modulus, MD (ASTM D882) in MPa (psi) 207 (30000)
2% Secant Modulus, TD (ASTM D882) in MPa (psi) 234 (34000)
Dart Drop Impact (ASTM D1709A) in grams (lbs) 66 g
Density 0.925 g/cm3
Elmendorf Tear Strength, MD (ASTM D1922) in grams (lbs) 280 g
Elmendorf Tear Strength, TD (ASTM D1922) in grams (lbs) 3000 g
Fabrication Method Blown Film Extrusion, Cast Film Extrusion
Functionality Optical Performance, Processing
Gloss (45 degree) 78
Haze (ASTM D1003) 5.4 %
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) 2
Puncture Resistance (Dow Method) in joules/cm3 (lbs/in3) 3.72 J/cm3 (45 ft /lb/in3)
Tensile Elongation at Break, MD 330 %
Tensile Elongation at Break, TD 550 %
Tensile Strength Break, MD (ASTM D882) in MPa (psi) 21.6 (3130)
Tensile Strength Break, TD (ASTM D882) in MPa (psi) 17 (3460)
Tensile Strength Yield, MD (ASTM D882) in MPa (psi) 13.5 (1960)
Tensile Strength Yield, TD (ASTM D882) in MPa (psi) 13.5 (1960)